| Fuerza de flexión | 50 MPa |
|---|---|
| Conductividad térmica | 105 W/mK |
| Densidad | 1.81 g/cm3 |
| La pureza | 99.95% |
| Coeficiente de expansión térmica | 5.4 x 10^-6 /K |
| Fuerza de flexión | 50 MPa |
|---|---|
| Conductividad térmica | 105 W/mK |
| Densidad | 1.81 g/cm3 |
| Purificación | 99.95% |
| Coeficiente de expansión térmica | 5.4 x 10^-6 /K |
| Bulk Density | 1.76 g/cm3 |
|---|---|
| Compressive Strength | 85 Mpa |
| Flexural Strength | 45 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 500/50 PPM |
| Bulk Density | 1.78 g/cm3 |
|---|---|
| Compressive Strength | 90 Mpa |
| Flexural Strength | 45 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 500/50 PPM |
| Densidad de volumen | 10,80 g/cm3 |
|---|---|
| Compressive Strength | 95 Mpa |
| Flexural Strength | 48 Mpa |
| resistencia eléctrica | 11 ~ 13 μΩ.m |
| Shore Hardness | 60 HSD |
| Densidad de volumen | 10,78 g/cm3 |
|---|---|
| Fuerza de compresión | 90 MPa |
| Flexural Strength | 45 Mpa |
| resistencia eléctrica | 11 ~ 13 μΩ.m |
| Contenido en cenizas | 500/50 ppm |
| Bulk Density | 1.76 g/cm3 |
|---|---|
| Fuerza de compresión | MPa 85 |
| Flexural Strength | 45 Mpa |
| resistencia eléctrica | 11 ~ 13 μΩ.m |
| Ash Content | 500/50 PPM |
| Densidad de volumen | 10,76 g/cm3 |
|---|---|
| Fuerza de compresión | MPa 85 |
| Fuerza de flexión | Mpa 45 |
| resistencia eléctrica | 11 ~ 13 μΩ.m |
| Contenido en cenizas | 500/50 ppm |
| Bulk Density | 1.80 g/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Fuerza de flexión | 50 MPa |
| Electric Resistance | 11~13 µΩ.m |
| Dureza de la orilla | 60 HSD |
| Densidad de volumen | 10,80 g/cm3 |
|---|---|
| Fuerza de compresión | Mpa 100 |
| Fuerza de flexión | 50 MPa |
| resistencia eléctrica | 11 ~ 13 μΩ.m |
| Dureza de la orilla | 60 HSD |