| Corrosion Resistance | Excellent |
|---|---|
| Purity | 99.95% |
| Chemical Resistance | High |
| Thermal Conductivity | 105 W/mK |
| Applications | Crucibles, Refractories, Foundry Coatings |
| Corrosion Resistance | Excellent |
|---|---|
| Purity | 99.95% |
| Chemical Resistance | High |
| Thermal Conductivity | 105 W/mK |
| Applications | Crucibles, Refractories, Foundry Coatings |
| Corrosion Resistance | Excellent |
|---|---|
| Purity | 99.95% |
| Chemical Resistance | High |
| Thermal Conductivity | 105 W/mK |
| Applications | Crucibles, Refractories, Foundry Coatings |
| Corrosion Resistance | Excellent |
|---|---|
| Purity | 99.95% |
| Chemical Resistance | High |
| Thermal Conductivity | 105 W/mK |
| Applications | Crucibles, Refractories, Foundry Coatings |
| Densidad de volumen | 10,78 g/cm3 |
|---|---|
| Fuerza de compresión | 105 MPa |
| Fuerza de flexión | 55 MPa |
| resistencia eléctrica | 13 ~ 14 μΩ.m |
| Dureza de la orilla | 68 HSD |
| Densidad de volumen | 10,78 g/cm3 |
|---|---|
| Fuerza de compresión | 105 MPa |
| Fuerza de flexión | 55 MPa |
| resistencia eléctrica | 13 ~ 14 μΩ.m |
| Dureza de la orilla | 68 HSD |
| Densidad de volumen | 10,82 g/cm3 |
|---|---|
| Fuerza de compresión | 110 MPa |
| Fuerza de flexión | 55 MPa |
| resistencia eléctrica | 13 ~ 14 μΩ.m |
| Dureza de la orilla | 68 HSD |
| Densidad de volumen | 10,82 g/cm3 |
|---|---|
| Fuerza de compresión | 110 MPa |
| Fuerza de flexión | 55 MPa |
| resistencia eléctrica | 13 ~ 14 μΩ.m |
| Dureza de la orilla | 68 HSD |
| Densidad de volumen | 10,71 g/cm3 |
|---|---|
| Fuerza de compresión | mpa 30 |
| Fuerza de flexión | Mpa 15 |
| resistencia eléctrica | 9 ~ 10 μΩ.m |
| Dureza de la orilla | 30 HSD |
| Densidad de volumen | 10,82 g/cm3 |
|---|---|
| Fuerza de compresión | 115 Mpa |
| Fuerza de flexión | Mpa 60 |
| resistencia eléctrica | 13 ~ 14 μΩ.m |
| Dureza de la orilla | 68 HSD |